Wipe wastes have been used as a cellulosic source to synthesize biochars. Prior to the synthesis of the adsorbents by the pyrolysis of wipes wastes, this waste was treated to remove the pathogenic agents. Then, the wipe wastes were pyrolyzed between 500 and 900 °C to obtain biochars, whose microporosity increased proportionally to the pyrolysis temperature, achieving a maximum CO2-adsorption uptake of 2.53 mmol/g at a pressure of 760 mm of Hg and 25 °C for the biochar pyrolized at 900 °C. The synthesized biochars are also highly selective towards CO2-adsorption in CO2/N2 or CO2/H2 mixtures. Hence, these adsorbents have shown a great potential to be used in flue gas treatment and H2-purification processes. Biochar treatment with KOH further improves microporosity due to chemical activation although the addition of a large amount of KOH leads to excessive microporosity causing a collapse in the pore structure and decreasing CO2-adsorption capacity.
RESUMO
Porous clay heterostructures (PCH) are obtained by the insertion of an organic bulky cation in the interlayer spacing of a smectite, causing a swelling of the clay mineral. Right after, oxides species, mainly silicon oxide, are incorporated as pillars galleries between adjacent layers to form a porous structure after the removal of the template. The ordering of the clay mineral as well the organic cation incorporated in the synthetic step favors the modulation of the textural properties of the PCH. In addition, the incorporation of heteroatoms in the pillars galleries can also modulate the acidity of the PCH. The modulation of the pore size and the acid properties provides to these materials a wide range of applications in the fields of adsorption and catalysis. This paper carries out a detailed review of the synthesis of PCH, characterization as well as uses and application reported in the literature.